Quarter-Hard (H01) C26800 Brass
H01 C26800 brass is C26800 brass in the H01 (quarter hard) temper. The graph bars on the material properties cards below compare H01 C26800 brass to: wrought brasses (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 15 x 106 psi
Elongation at Break
22 %
Poisson's Ratio
0.31
Rockwell B Hardness
53
Shear Modulus
40 GPa 5.9 x 106 psi
Shear Strength
230 MPa 34 x 103 psi
Tensile Strength: Ultimate (UTS)
370 MPa 54 x 103 psi
Tensile Strength: Yield (Proof)
190 MPa 27 x 103 psi
Thermal Properties
Latent Heat of Fusion
180 J/g
Maximum Temperature: Mechanical
130 °C 270 °F
Melting Completion (Liquidus)
930 °C 1710 °F
Melting Onset (Solidus)
900 °C 1660 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
120 W/m-K 67 BTU/h-ft-°F
Thermal Expansion
20 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
27 % IACS
Electrical Conductivity: Equal Weight (Specific)
30 % IACS
Otherwise Unclassified Properties
Base Metal Price
24 % relative
Calomel Potential
-360 mV
Density
8.1 g/cm3 510 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
45 MJ/kg 19 x 103 BTU/lb
Embodied Water
320 L/kg 38 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
68 MJ/m3
Resilience: Unit (Modulus of Resilience)
170 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
13 points
Strength to Weight: Bending
14 points
Thermal Diffusivity
37 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Cu | 64 to 68.5 | |
| Zn | 31 to 36 | |
| Pb | 0 to 0.15 | |
| Fe | 0 to 0.050 | |
| res. | 0 to 0.3 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B36: Standard Specification for Brass Plate, Sheet, Strip, And Rolled Bar
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993