Quarter-Hard (H01) C75700 Nickel Silver
H01 C75700 nickel silver is C75700 nickel silver in the H01 (quarter hard) temper. The graph bars on the material properties cards below compare H01 C75700 nickel silver to: wrought copper-nickels (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
22 %
Poisson's Ratio
0.32
Shear Modulus
45 GPa 6.5 x 106 psi
Shear Strength
370 MPa 53 x 103 psi
Tensile Strength: Ultimate (UTS)
590 MPa 85 x 103 psi
Tensile Strength: Yield (Proof)
470 MPa 68 x 103 psi
Thermal Properties
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
180 °C 350 °F
Melting Completion (Liquidus)
1040 °C 1900 °F
Melting Onset (Solidus)
990 °C 1810 °F
Specific Heat Capacity
390 J/kg-K 0.094 BTU/lb-°F
Thermal Conductivity
40 W/m-K 23 BTU/h-ft-°F
Thermal Expansion
16 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
8.0 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.6 % IACS
Otherwise Unclassified Properties
Base Metal Price
30 % relative
Density
8.4 g/cm3 520 lb/ft3
Embodied Carbon
3.6 kg CO2/kg material
Embodied Energy
56 MJ/kg 24 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
120 MJ/m3
Resilience: Unit (Modulus of Resilience)
930 kJ/m3
Stiffness to Weight: Axial
7.8 points
Stiffness to Weight: Bending
19 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
19 points
Thermal Diffusivity
12 mm2/s
Thermal Shock Resistance
22 points
Alloy Composition
| Cu | 63.5 to 66.5 | |
| Zn | 19.2 to 25.5 | |
| Ni | 11 to 13 | |
| Mn | 0 to 0.5 | |
| Fe | 0 to 0.25 | |
| Pb | 0 to 0.050 | |
| res. | 0 to 0.5 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B151: Standard Specification for Copper-Nickel-Zinc Alloy (Nickel Silver) and Copper-Nickel Rod and Bar
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001