Quenched and Tempered (+QT) 1.1170 Steel
EN 1.1170 +QT steel is EN 1.1170 steel in the quenched and tempered condition. The graph bars on the material properties cards below compare EN 1.1170 +QT steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
210
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
16 %
Fatigue Strength
330 MPa 48 x 103 psi
Impact Strength: V-Notched Charpy
35 J 25 ft-lb
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
450 MPa 65 x 103 psi
Tensile Strength: Ultimate (UTS)
730 MPa 110 x 103 psi
Tensile Strength: Yield (Proof)
500 MPa 73 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
50 W/m-K 29 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.4 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.1 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.5 kg CO2/kg material
Embodied Energy
19 MJ/kg 8.3 x 103 BTU/lb
Embodied Water
49 L/kg 5.8 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
100 MJ/m3
Resilience: Unit (Modulus of Resilience)
670 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
13 mm2/s
Thermal Shock Resistance
23 points
Alloy Composition
| Fe | 96.7 to 98.5 | |
| Mn | 1.3 to 1.7 | |
| C | 0.25 to 0.32 | |
| Si | 0 to 0.4 | |
| Cr | 0 to 0.4 | |
| Ni | 0 to 0.4 | |
| Mo | 0 to 0.1 | |
| P | 0 to 0.035 | |
| S | 0 to 0.035 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10250-2: Open die steel forgings for general engineering purposes - Part 2: Non-alloy quality and special steels
Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004
Carbon Steel Handbook, D. Gandy, 2007
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015