Quenched and Tempered (+QT) 1.5507 Steel
EN 1.5507 +QT steel is EN 1.5507 steel in the quenched and tempered condition. The graph bars on the material properties cards below compare EN 1.5507 +QT steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
260
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
16 %
Fatigue Strength
480 MPa 70 x 103 psi
Impact Strength: V-Notched Charpy
46 J 34 ft-lb
Poisson's Ratio
0.29
Reduction in Area
58 %
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
540 MPa 78 x 103 psi
Tensile Strength: Ultimate (UTS)
880 MPa 130 x 103 psi
Tensile Strength: Yield (Proof)
730 MPa 110 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
410 °C 760 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
49 W/m-K 28 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.2 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.0 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
19 MJ/kg 8.1 x 103 BTU/lb
Embodied Water
49 L/kg 5.8 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
130 MJ/m3
Resilience: Unit (Modulus of Resilience)
1420 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
31 points
Strength to Weight: Bending
26 points
Thermal Diffusivity
13 mm2/s
Thermal Shock Resistance
26 points
Alloy Composition
| Fe | 97.8 to 98.7 | |
| Mn | 0.8 to 1.0 | |
| Cr | 0.25 to 0.35 | |
| C | 0.21 to 0.25 | |
| Cu | 0 to 0.25 | |
| Si | 0 to 0.15 | |
| Al | 0.020 to 0.080 | |
| Ti | 0 to 0.060 | |
| P | 0 to 0.015 | |
| S | 0 to 0.015 | |
| B | 0.00080 to 0.0050 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10269: Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
Boron in Steel, S. K. Banerji and J. E. Morral (editors), 1980
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015