SAE-AISI 8822 (G88220) Ni-Cr-Mo Steel
SAE-AISI 8822 steel is an alloy steel formulated for primary forming into wrought products. Cited properties are appropriate for the annealed condition. 8822 is the designation in both the SAE and AISI systems for this material. G88220 is the UNS number.
It has a moderately low thermal conductivity among the SAE-AISI wrought steels in the database.
The graph bars on the material properties cards below compare SAE-AISI 8822 steel to: SAE-AISI wrought steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
160
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
23 %
Fatigue Strength
270 MPa 38 x 103 psi
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Shear Strength
340 MPa 49 x 103 psi
Tensile Strength: Ultimate (UTS)
540 MPa 78 x 103 psi
Tensile Strength: Yield (Proof)
370 MPa 54 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
420 °C 780 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
38 W/m-K 22 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.3 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.4 % IACS
Otherwise Unclassified Properties
Base Metal Price
2.8 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.6 kg CO2/kg material
Embodied Energy
21 MJ/kg 8.9 x 103 BTU/lb
Embodied Water
50 L/kg 6.0 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m3
Resilience: Unit (Modulus of Resilience)
360 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
19 points
Thermal Diffusivity
10 mm2/s
Thermal Shock Resistance
18 points
Alloy Composition
Among alloy steels, the composition of SAE-AISI 8822 steel is notable for including nickel (Ni). Nickel is used to improve mechanical properties, and to make the alloy easier to heat treat.
| Fe | 96.6 to 97.8 | |
| Mn | 0.75 to 1.0 | |
| Ni | 0.4 to 0.7 | |
| Cr | 0.4 to 0.6 | |
| Mo | 0.3 to 0.4 | |
| Si | 0.15 to 0.35 | |
| C | 0.2 to 0.25 | |
| S | 0 to 0.040 | |
| P | 0 to 0.035 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
ASTM A752: Standard Specification for General Requirements for Wire Rods and Coarse Round Wire, Alloy Steel
ASTM A322: Standard Specification for Steel Bars, Alloy, Standard Grades
ASM Specialty Handbook: Carbon and Alloy Steels, J. R. Davis (editor), 1996
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015