Soft Annealed (O60) C31400 Bronze
O60 C31400 bronze is C31400 bronze in the O60 (soft annealed) temper. It has the lowest strength and highest ductility compared to the other variants of C31400 bronze. The graph bars on the material properties cards below compare O60 C31400 bronze to: wrought bronzes (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
110 GPa 16 x 106 psi
Elongation at Break
29 %
Poisson's Ratio
0.33
Shear Modulus
42 GPa 6.1 x 106 psi
Shear Strength
180 MPa 26 x 103 psi
Tensile Strength: Ultimate (UTS)
270 MPa 40 x 103 psi
Tensile Strength: Yield (Proof)
78 MPa 11 x 103 psi
Thermal Properties
Latent Heat of Fusion
200 J/g
Maximum Temperature: Mechanical
180 °C 350 °F
Melting Completion (Liquidus)
1040 °C 1900 °F
Melting Onset (Solidus)
1010 °C 1850 °F
Specific Heat Capacity
380 J/kg-K 0.091 BTU/lb-°F
Thermal Conductivity
180 W/m-K 100 BTU/h-ft-°F
Thermal Expansion
18 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
42 % IACS
Electrical Conductivity: Equal Weight (Specific)
43 % IACS
Otherwise Unclassified Properties
Base Metal Price
29 % relative
Density
8.8 g/cm3 550 lb/ft3
Embodied Carbon
2.6 kg CO2/kg material
Embodied Energy
42 MJ/kg 18 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
59 MJ/m3
Resilience: Unit (Modulus of Resilience)
28 kJ/m3
Stiffness to Weight: Axial
7.1 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
8.7 points
Strength to Weight: Bending
11 points
Thermal Diffusivity
54 mm2/s
Thermal Shock Resistance
9.6 points
Alloy Composition
| Cu | 87.5 to 90.5 | |
| Zn | 5.8 to 11.2 | |
| Pb | 1.3 to 2.5 | |
| Ni | 0 to 0.7 | |
| Fe | 0 to 0.1 | |
| res. | 0 to 0.4 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B140: Standard Specification for Copper-Zinc-Lead (Red Brass or Hardware Bronze) Rod, Bar, and Shapes
ASM Specialty Handbook: Copper and Copper Alloys, J. R. Davis (editor), 2001