Spheroidized (+AC) 1.5511 Steel
EN 1.5511 +AC steel is EN 1.5511 steel in the spheroidized condition. The graph bars on the material properties cards below compare EN 1.5511 +AC steel to: EN wrought alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
150
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Poisson's Ratio
0.29
Reduction in Area
69 %
Shear Modulus
72 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
490 MPa 71 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2580 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
51 W/m-K 30 BTU/h-ft-°F
Thermal Expansion
13 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.1 % IACS
Otherwise Unclassified Properties
Base Metal Price
1.8 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
19 MJ/kg 8.0 x 103 BTU/lb
Embodied Water
46 L/kg 5.5 gal/lb
Common Calculations
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
17 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
14 mm2/s
Thermal Shock Resistance
15 points
Alloy Composition
| Fe | 98.3 to 99.159 | |
| Mn | 0.5 to 0.8 | |
| C | 0.32 to 0.39 | |
| Si | 0 to 0.4 | |
| Al | 0.020 to 0.060 | |
| P | 0 to 0.030 | |
| S | 0 to 0.015 | |
| B | 0.00080 to 0.0050 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
EN 10269: Steels and nickel alloys for fasteners with specified elevated and/or low temperature properties
Boron in Steel, S. K. Banerji and J. E. Morral (editors), 1980
Manufacture and Uses of Alloy Steels, Henry D. Hibbard, 2005
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015