TH02 Tempered C15000 Copper
TH02 C15000 copper is C15000 copper in the TH02 (half-hard and precipitation heat treated) temper. The graph bars on the material properties cards below compare TH02 C15000 copper to: wrought coppers (top), all copper alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
120 GPa 17 x 106 psi
Elongation at Break
23 %
Poisson's Ratio
0.34
Rockwell F Hardness
90
Shear Modulus
43 GPa 6.3 x 106 psi
Shear Strength
230 MPa 34 x 103 psi
Tensile Strength: Ultimate (UTS)
370 MPa 53 x 103 psi
Tensile Strength: Yield (Proof)
370 MPa 53 x 103 psi
Thermal Properties
Latent Heat of Fusion
210 J/g
Maximum Temperature: Mechanical
200 °C 390 °F
Melting Completion (Liquidus)
1080 °C 1980 °F
Melting Onset (Solidus)
980 °C 1800 °F
Specific Heat Capacity
390 J/kg-K 0.092 BTU/lb-°F
Thermal Conductivity
370 W/m-K 210 BTU/h-ft-°F
Thermal Expansion
17 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
93 % IACS
Electrical Conductivity: Equal Weight (Specific)
93 % IACS
Otherwise Unclassified Properties
Base Metal Price
31 % relative
Density
9.0 g/cm3 560 lb/ft3
Embodied Carbon
2.7 kg CO2/kg material
Embodied Energy
43 MJ/kg 19 x 103 BTU/lb
Embodied Water
310 L/kg 37 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
84 MJ/m3
Resilience: Unit (Modulus of Resilience)
580 kJ/m3
Stiffness to Weight: Axial
7.2 points
Stiffness to Weight: Bending
18 points
Strength to Weight: Axial
11 points
Strength to Weight: Bending
13 points
Thermal Diffusivity
110 mm2/s
Thermal Shock Resistance
13 points
Alloy Composition
| Cu | 99.8 to 99.9 | |
| Zr | 0.1 to 0.2 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Copper: Its Trade, Manufacture, Use, and Environmental Status, Gunter Joseph, 2001
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993