201.0 Aluminum vs. AISI 202 Stainless Steel

201.0 aluminum belongs to the aluminum alloys classification, while AISI 202 stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 201.0 aluminum and the bottom bar is AISI 202 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 95 to 140
210 to 300
Elastic (Young's, Tensile) Modulus, GPa 71
200
Elongation at Break, % 4.4 to 20
14 to 45
Fatigue Strength, MPa 120 to 150
290 to 330
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
77
Shear Strength, MPa 290
490 to 590
Tensile Strength: Ultimate (UTS), MPa 370 to 470
700 to 980
Tensile Strength: Yield (Proof), MPa 220 to 400
310 to 580

Thermal Properties

Latent Heat of Fusion, J/g 390
290
Maximum Temperature: Mechanical, °C 170
910
Melting Completion (Liquidus), °C 650
1400
Melting Onset (Solidus), °C 570
1360
Specific Heat Capacity, J/kg-K 870
480
Thermal Conductivity, W/m-K 120
15
Thermal Expansion, µm/m-K 19
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30 to 33
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 87 to 97
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 38
13
Density, g/cm3 3.1
7.7
Embodied Carbon, kg CO2/kg material 8.7
2.8
Embodied Energy, MJ/kg 160
40

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 19 to 63
120 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 1160
250 to 840
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 45
25
Strength to Weight: Axial, points 33 to 42
25 to 35
Strength to Weight: Bending, points 37 to 44
23 to 29
Thermal Diffusivity, mm2/s 45
4.0
Thermal Shock Resistance, points 19 to 25
15 to 21

Alloy Composition

Aluminum (Al), % 92.1 to 95.1
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 4.0 to 5.2
0
Iron (Fe), % 0 to 0.15
63.5 to 71.5
Magnesium (Mg), % 0.15 to 0.55
0
Manganese (Mn), % 0.2 to 0.5
7.5 to 10
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0
0 to 0.060
Silicon (Si), % 0 to 0.1
0 to 1.0
Silver (Ag), % 0.4 to 1.0
0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0.15 to 0.35
0
Residuals, % 0 to 0.1
0