213.0 Aluminum vs. AISI 201LN Stainless Steel

213.0 aluminum belongs to the aluminum alloys classification, while AISI 201LN stainless steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 213.0 aluminum and the bottom bar is AISI 201LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 85
210 to 320
Elastic (Young's, Tensile) Modulus, GPa 73
200
Elongation at Break, % 1.5
25 to 51
Fatigue Strength, MPa 93
340 to 540
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 28
77
Tensile Strength: Ultimate (UTS), MPa 190
740 to 1060
Tensile Strength: Yield (Proof), MPa 130
350 to 770

Thermal Properties

Latent Heat of Fusion, J/g 410
280
Maximum Temperature: Mechanical, °C 170
880
Melting Completion (Liquidus), °C 670
1410
Melting Onset (Solidus), °C 480
1370
Specific Heat Capacity, J/kg-K 850
480
Thermal Conductivity, W/m-K 130
15
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 34
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 94
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 11
12
Density, g/cm3 3.2
7.7
Embodied Carbon, kg CO2/kg material 7.7
2.6
Embodied Energy, MJ/kg 140
38
Embodied Water, L/kg 1090
140

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.5
230 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 120
310 to 1520
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 44
25
Strength to Weight: Axial, points 16
27 to 38
Strength to Weight: Bending, points 23
24 to 30
Thermal Diffusivity, mm2/s 49
4.0
Thermal Shock Resistance, points 8.0
16 to 23

Alloy Composition

Aluminum (Al), % 83.5 to 93
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
16 to 17.5
Copper (Cu), % 6.0 to 8.0
0 to 1.0
Iron (Fe), % 0 to 1.2
67.9 to 73.5
Magnesium (Mg), % 0 to 0.1
0
Manganese (Mn), % 0 to 0.6
6.4 to 7.5
Nickel (Ni), % 0 to 0.35
4.0 to 5.0
Nitrogen (N), % 0
0.1 to 0.25
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 1.0 to 3.0
0 to 0.75
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0 to 0.25
0
Zinc (Zn), % 0 to 2.5
0
Residuals, % 0 to 0.5
0