224.0 Aluminum vs. 5383 Aluminum
Both 224.0 aluminum and 5383 aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 224.0 aluminum and the bottom bar is 5383 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 68 |
| Elongation at Break, % | 4.0 to 10 | |
| 6.7 to 15 |
| Fatigue Strength, MPa | 86 to 120 | |
| 130 to 200 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 420 | |
| 310 to 370 |
| Tensile Strength: Yield (Proof), MPa | 280 to 330 | |
| 150 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 200 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 550 | |
| 540 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 29 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 97 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 9.0 |
| Embodied Energy, MJ/kg | 160 | |
| 160 |
| Embodied Water, L/kg | 1150 | |
| 1170 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 35 | |
| 23 to 40 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 to 770 | |
| 170 to 690 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 45 | |
| 50 |
| Strength to Weight: Axial, points | 35 to 38 | |
| 32 to 38 |
| Strength to Weight: Bending, points | 38 to 41 | |
| 38 to 42 |
| Thermal Diffusivity, mm2/s | 47 | |
| 51 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 14 to 16 |
Alloy Composition
| Aluminum (Al), % | 93 to 95.2 | |
| 92 to 95.3 |
| Chromium (Cr), % | 0 | |
| 0 to 0.25 |
| Copper (Cu), % | 4.5 to 5.5 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0 | |
| 4.0 to 5.2 |
| Manganese (Mn), % | 0.2 to 0.5 | |
| 0.7 to 1.0 |
| Silicon (Si), % | 0 to 0.060 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.35 | |
| 0 to 0.15 |
| Vanadium (V), % | 0.050 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.4 |
| Zirconium (Zr), % | 0.1 to 0.25 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |