224.0 Aluminum vs. EV31A Magnesium
224.0 aluminum belongs to the aluminum alloys classification, while EV31A magnesium belongs to the magnesium alloys. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is 224.0 aluminum and the bottom bar is EV31A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 44 |
| Elongation at Break, % | 4.0 to 10 | |
| 3.5 |
| Fatigue Strength, MPa | 86 to 120 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.27 |
| Shear Modulus, GPa | 27 | |
| 17 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 420 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 280 to 330 | |
| 170 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 220 | |
| 200 |
| Melting Onset (Solidus), °C | 550 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 1000 |
| Thermal Conductivity, W/m-K | 120 | |
| 86 |
| Thermal Expansion, µm/m-K | 23 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 32 | |
| 18 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 90 |
Otherwise Unclassified Properties
| Density, g/cm3 | 3.0 | |
| 1.8 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 35 | |
| 8.1 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 540 to 770 | |
| 330 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 45 | |
| 65 |
| Strength to Weight: Axial, points | 35 to 38 | |
| 40 |
| Strength to Weight: Bending, points | 38 to 41 | |
| 50 |
| Thermal Diffusivity, mm2/s | 47 | |
| 47 |
| Thermal Shock Resistance, points | 17 to 18 | |
| 16 |