238.0 Aluminum vs. 6101B Aluminum
Both 238.0 aluminum and 6101B aluminum are aluminum alloys. They have 84% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 238.0 aluminum and the bottom bar is 6101B aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 76 | |
| 68 |
| Elongation at Break, % | 1.5 | |
| 9.1 to 13 |
| Fatigue Strength, MPa | 110 | |
| 62 to 70 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 28 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 210 | |
| 190 to 250 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 140 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 430 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 600 | |
| 640 |
| Melting Onset (Solidus), °C | 510 | |
| 630 |
| Specific Heat Capacity, J/kg-K | 840 | |
| 900 |
| Thermal Conductivity, W/m-K | 100 | |
| 210 |
| Thermal Expansion, µm/m-K | 21 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 57 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 67 | |
| 190 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 9.5 |
| Density, g/cm3 | 3.4 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 7.4 | |
| 8.3 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1040 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.9 | |
| 20 to 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 140 to 240 |
| Stiffness to Weight: Axial, points | 12 | |
| 14 |
| Stiffness to Weight: Bending, points | 42 | |
| 50 |
| Strength to Weight: Axial, points | 17 | |
| 20 to 25 |
| Strength to Weight: Bending, points | 23 | |
| 27 to 32 |
| Thermal Diffusivity, mm2/s | 37 | |
| 87 |
| Thermal Shock Resistance, points | 9.1 | |
| 8.5 to 11 |
Alloy Composition
| Aluminum (Al), % | 81.9 to 84.9 | |
| 98.2 to 99.3 |
| Copper (Cu), % | 9.5 to 10.5 | |
| 0 to 0.050 |
| Iron (Fe), % | 1.0 to 1.5 | |
| 0.1 to 0.3 |
| Magnesium (Mg), % | 0 to 0.25 | |
| 0.35 to 0.6 |
| Manganese (Mn), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 3.6 to 4.4 | |
| 0.3 to 0.6 |
| Zinc (Zn), % | 1.0 to 1.5 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.1 |