3003 Aluminum vs. C87300 Bronze

3003 aluminum belongs to the aluminum alloys classification, while C87300 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 3003 aluminum and the bottom bar is C87300 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
120
Elongation at Break, % 1.1 to 28
22
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
43
Tensile Strength: Ultimate (UTS), MPa 110 to 240
350
Tensile Strength: Yield (Proof), MPa 40 to 210
140

Thermal Properties

Latent Heat of Fusion, J/g 400
280
Maximum Temperature: Mechanical, °C 180
200
Melting Completion (Liquidus), °C 650
970
Melting Onset (Solidus), °C 640
820
Specific Heat Capacity, J/kg-K 900
410
Thermal Conductivity, W/m-K 180
28
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 44
6.1
Electrical Conductivity: Equal Weight (Specific), % IACS 140
6.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
29
Density, g/cm3 2.8
8.6
Embodied Carbon, kg CO2/kg material 8.1
2.7
Embodied Energy, MJ/kg 150
42
Embodied Water, L/kg 1180
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 0.95 to 63
62
Resilience: Unit (Modulus of Resilience), kJ/m3 11 to 300
86
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 50
19
Strength to Weight: Axial, points 11 to 24
11
Strength to Weight: Bending, points 18 to 30
13
Thermal Diffusivity, mm2/s 71
8.0
Thermal Shock Resistance, points 4.7 to 10
13

Alloy Composition

Aluminum (Al), % 96.8 to 99
0
Copper (Cu), % 0.050 to 0.2
94 to 95.7
Iron (Fe), % 0 to 0.7
0 to 0.2
Lead (Pb), % 0
0 to 0.2
Manganese (Mn), % 1.0 to 1.5
0.8 to 1.5
Silicon (Si), % 0 to 0.6
3.5 to 5.0
Zinc (Zn), % 0 to 0.1
0 to 0.25
Residuals, % 0
0 to 0.5