3102 Aluminum vs. A384.0 Aluminum
Both 3102 aluminum and A384.0 aluminum are aluminum alloys. They have 84% of their average alloy composition in common.
For each property being compared, the top bar is 3102 aluminum and the bottom bar is A384.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 74 |
| Elongation at Break, % | 23 to 28 | |
| 2.5 |
| Fatigue Strength, MPa | 31 to 34 | |
| 140 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 28 |
| Shear Strength, MPa | 58 to 65 | |
| 200 |
| Tensile Strength: Ultimate (UTS), MPa | 92 to 100 | |
| 330 |
| Tensile Strength: Yield (Proof), MPa | 28 to 34 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 550 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 610 |
| Melting Onset (Solidus), °C | 640 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 880 |
| Thermal Conductivity, W/m-K | 230 | |
| 96 |
| Thermal Expansion, µm/m-K | 23 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 56 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 | |
| 73 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.0 | |
| 11 |
| Density, g/cm3 | 2.7 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 7.5 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1190 | |
| 1010 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 22 | |
| 6.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 5.8 to 8.3 | |
| 180 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 9.4 to 10 | |
| 32 |
| Strength to Weight: Bending, points | 17 to 18 | |
| 38 |
| Thermal Diffusivity, mm2/s | 92 | |
| 39 |
| Thermal Shock Resistance, points | 4.1 to 4.4 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 97.9 to 99.95 | |
| 79.3 to 86.5 |
| Copper (Cu), % | 0 to 0.1 | |
| 3.0 to 4.5 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 1.3 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.1 |
| Manganese (Mn), % | 0.050 to 0.4 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.5 |
| Silicon (Si), % | 0 to 0.4 | |
| 10.5 to 12 |
| Tin (Sn), % | 0 | |
| 0 to 0.35 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |