3105 Aluminum vs. ASTM A588 Steel
3105 aluminum belongs to the aluminum alloys classification, while ASTM A588 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 3105 aluminum and the bottom bar is ASTM A588 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 29 to 67 | |
| 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 190 |
| Elongation at Break, % | 1.1 to 20 | |
| 22 |
| Fatigue Strength, MPa | 39 to 95 | |
| 270 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 73 |
| Shear Strength, MPa | 77 to 140 | |
| 350 |
| Tensile Strength: Ultimate (UTS), MPa | 120 to 240 | |
| 550 |
| Tensile Strength: Yield (Proof), MPa | 46 to 220 | |
| 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 to 260 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 410 |
| Melting Completion (Liquidus), °C | 660 | |
| 1460 |
| Melting Onset (Solidus), °C | 640 | |
| 1410 to 1420 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 470 |
| Thermal Conductivity, W/m-K | 170 | |
| 43 to 44 |
| Thermal Expansion, µm/m-K | 24 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 44 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 2.3 to 2.5 |
| Density, g/cm3 | 2.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 1.5 to 1.6 |
| Embodied Energy, MJ/kg | 150 | |
| 20 to 22 |
| Embodied Water, L/kg | 1180 | |
| 50 to 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.6 to 19 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 15 to 340 | |
| 400 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 24 |
| Strength to Weight: Axial, points | 12 to 24 | |
| 20 |
| Strength to Weight: Bending, points | 20 to 31 | |
| 19 |
| Thermal Diffusivity, mm2/s | 68 | |
| 12 |
| Thermal Shock Resistance, points | 5.2 to 11 | |
| 16 |