3105 Aluminum vs. EN 1.0434 Steel
3105 aluminum belongs to the aluminum alloys classification, while EN 1.0434 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 3105 aluminum and the bottom bar is EN 1.0434 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 29 to 67 | |
| 110 to 160 |
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 190 |
| Elongation at Break, % | 1.1 to 20 | |
| 12 to 28 |
| Fatigue Strength, MPa | 39 to 95 | |
| 190 to 300 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 73 |
| Shear Strength, MPa | 77 to 140 | |
| 280 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 120 to 240 | |
| 390 to 540 |
| Tensile Strength: Yield (Proof), MPa | 46 to 220 | |
| 250 to 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 400 |
| Melting Completion (Liquidus), °C | 660 | |
| 1460 |
| Melting Onset (Solidus), °C | 640 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 470 |
| Thermal Conductivity, W/m-K | 170 | |
| 52 |
| Thermal Expansion, µm/m-K | 24 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 44 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 1.8 |
| Density, g/cm3 | 2.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 150 | |
| 18 |
| Embodied Water, L/kg | 1180 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.6 to 19 | |
| 39 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 15 to 340 | |
| 170 to 540 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 24 |
| Strength to Weight: Axial, points | 12 to 24 | |
| 14 to 19 |
| Strength to Weight: Bending, points | 20 to 31 | |
| 15 to 19 |
| Thermal Diffusivity, mm2/s | 68 | |
| 14 |
| Thermal Shock Resistance, points | 5.2 to 11 | |
| 12 to 17 |
Alloy Composition
| Aluminum (Al), % | 96 to 99.5 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 | |
| 0.15 to 0.19 |
| Chromium (Cr), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 0 to 0.7 | |
| 98.8 to 99.18 |
| Magnesium (Mg), % | 0.2 to 0.8 | |
| 0 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0.65 to 0.85 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.4 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |