319.0 Aluminum vs. EN 1.5503 Steel

319.0 aluminum belongs to the aluminum alloys classification, while EN 1.5503 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 319.0 aluminum and the bottom bar is EN 1.5503 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 78 to 84
120 to 160
Elastic (Young's, Tensile) Modulus, GPa 72
190
Elongation at Break, % 1.8 to 2.0
12 to 17
Fatigue Strength, MPa 76 to 80
180 to 280
Poisson's Ratio 0.33
0.29
Shear Modulus, GPa 27
73
Shear Strength, MPa 170 to 210
270 to 320
Tensile Strength: Ultimate (UTS), MPa 190 to 240
400 to 520
Tensile Strength: Yield (Proof), MPa 110 to 180
270 to 430

Thermal Properties

Latent Heat of Fusion, J/g 480
250
Maximum Temperature: Mechanical, °C 170
400
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 540
1420
Specific Heat Capacity, J/kg-K 880
470
Thermal Conductivity, W/m-K 110
52
Thermal Expansion, µm/m-K 22
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 27
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 84
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 10
1.8
Density, g/cm3 2.9
7.8
Embodied Carbon, kg CO2/kg material 7.7
1.4
Embodied Energy, MJ/kg 140
18
Embodied Water, L/kg 1080
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 3.3 to 3.9
41 to 81
Resilience: Unit (Modulus of Resilience), kJ/m3 88 to 220
200 to 490
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 48
24
Strength to Weight: Axial, points 18 to 24
14 to 19
Strength to Weight: Bending, points 25 to 30
15 to 18
Thermal Diffusivity, mm2/s 44
14
Thermal Shock Resistance, points 8.6 to 11
12 to 15

Alloy Composition

Aluminum (Al), % 85.8 to 91.5
0
Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0
0.16 to 0.2
Copper (Cu), % 3.0 to 4.0
0 to 0.25
Iron (Fe), % 0 to 1.0
98.4 to 99.239
Magnesium (Mg), % 0 to 0.1
0
Manganese (Mn), % 0 to 0.5
0.6 to 0.8
Nickel (Ni), % 0 to 0.35
0
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 5.5 to 6.5
0 to 0.3
Sulfur (S), % 0
0 to 0.025
Titanium (Ti), % 0 to 0.25
0
Zinc (Zn), % 0 to 1.0
0
Residuals, % 0 to 0.5
0