328.0 Aluminum vs. 5182 Aluminum
Both 328.0 aluminum and 5182 aluminum are aluminum alloys. They have 89% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 328.0 aluminum and the bottom bar is 5182 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 68 |
| Elongation at Break, % | 1.6 to 2.1 | |
| 1.1 to 12 |
| Fatigue Strength, MPa | 55 to 80 | |
| 100 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 25 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 270 | |
| 280 to 420 |
| Tensile Strength: Yield (Proof), MPa | 120 to 170 | |
| 130 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 510 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 180 |
| Melting Completion (Liquidus), °C | 620 | |
| 640 |
| Melting Onset (Solidus), °C | 560 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 130 |
| Thermal Expansion, µm/m-K | 22 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 94 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 8.9 |
| Embodied Energy, MJ/kg | 140 | |
| 150 |
| Embodied Water, L/kg | 1070 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.8 to 5.0 | |
| 2.6 to 49 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 92 to 200 | |
| 120 to 950 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 51 | |
| 51 |
| Strength to Weight: Axial, points | 21 to 28 | |
| 29 to 44 |
| Strength to Weight: Bending, points | 28 to 34 | |
| 36 to 47 |
| Thermal Diffusivity, mm2/s | 50 | |
| 53 |
| Thermal Shock Resistance, points | 9.2 to 12 | |
| 12 to 19 |
Alloy Composition
| Aluminum (Al), % | 84.5 to 91.1 | |
| 93.2 to 95.8 |
| Chromium (Cr), % | 0 to 0.35 | |
| 0 to 0.1 |
| Copper (Cu), % | 1.0 to 2.0 | |
| 0 to 0.15 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.35 |
| Magnesium (Mg), % | 0.2 to 0.6 | |
| 4.0 to 5.0 |
| Manganese (Mn), % | 0.2 to 0.6 | |
| 0.2 to 0.5 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 |
| Silicon (Si), % | 7.5 to 8.5 | |
| 0 to 0.2 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 1.5 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |