332.0 Aluminum vs. C79600 Nickel Silver

332.0 aluminum belongs to the aluminum alloys classification, while C79600 nickel silver belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 332.0 aluminum and the bottom bar is C79600 nickel silver.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 73
110
Elongation at Break, % 1.0
15
Poisson's Ratio 0.33
0.3
Shear Modulus, GPa 27
43
Shear Strength, MPa 190
290
Tensile Strength: Ultimate (UTS), MPa 250
480
Tensile Strength: Yield (Proof), MPa 190
300

Thermal Properties

Latent Heat of Fusion, J/g 530
180
Maximum Temperature: Mechanical, °C 170
130
Melting Completion (Liquidus), °C 580
930
Melting Onset (Solidus), °C 530
880
Specific Heat Capacity, J/kg-K 880
390
Thermal Conductivity, W/m-K 100
36
Thermal Expansion, µm/m-K 21
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 26
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 84
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 10
25
Density, g/cm3 2.8
7.9
Embodied Carbon, kg CO2/kg material 7.8
3.5
Embodied Energy, MJ/kg 140
57
Embodied Water, L/kg 1040
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.3
63
Resilience: Unit (Modulus of Resilience), kJ/m3 250
400
Stiffness to Weight: Axial, points 15
7.8
Stiffness to Weight: Bending, points 50
20
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 31
17
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 12
15

Alloy Composition

Aluminum (Al), % 80.1 to 89
0
Copper (Cu), % 2.0 to 4.0
43.5 to 46.5
Iron (Fe), % 0 to 1.2
0
Lead (Pb), % 0
0.8 to 1.2
Magnesium (Mg), % 0.5 to 1.5
0
Manganese (Mn), % 0 to 0.5
1.5 to 2.5
Nickel (Ni), % 0 to 0.5
9.0 to 11
Silicon (Si), % 8.5 to 10.5
0
Titanium (Ti), % 0 to 0.25
0
Zinc (Zn), % 0 to 1.0
38.3 to 45.2
Residuals, % 0
0 to 0.5