333.0 Aluminum vs. ISO-WD21150 Magnesium
333.0 aluminum belongs to the aluminum alloys classification, while ISO-WD21150 magnesium belongs to the magnesium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is 333.0 aluminum and the bottom bar is ISO-WD21150 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 73 | |
| 45 |
| Elongation at Break, % | 1.0 to 2.0 | |
| 5.7 to 11 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 28 | |
| 17 |
| Shear Strength, MPa | 190 to 230 | |
| 150 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 230 to 280 | |
| 240 to 290 |
| Tensile Strength: Yield (Proof), MPa | 130 to 210 | |
| 120 to 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 520 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 110 |
| Melting Completion (Liquidus), °C | 590 | |
| 600 |
| Melting Onset (Solidus), °C | 530 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 990 |
| Thermal Conductivity, W/m-K | 100 to 140 | |
| 100 |
| Thermal Expansion, µm/m-K | 21 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 26 to 35 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 83 to 110 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 10 | |
| 12 |
| Density, g/cm3 | 2.8 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 7.6 | |
| 23 |
| Embodied Energy, MJ/kg | 140 | |
| 160 |
| Embodied Water, L/kg | 1040 | |
| 980 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.1 to 4.6 | |
| 15 to 24 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 290 | |
| 160 to 460 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 49 | |
| 70 |
| Strength to Weight: Axial, points | 22 to 27 | |
| 40 to 48 |
| Strength to Weight: Bending, points | 29 to 34 | |
| 52 to 58 |
| Thermal Diffusivity, mm2/s | 42 to 57 | |
| 60 |
| Thermal Shock Resistance, points | 11 to 13 | |
| 15 to 17 |
Alloy Composition
| Aluminum (Al), % | 81.8 to 89 | |
| 2.4 to 3.6 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 to 1.0 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0.050 to 0.5 | |
| 94 to 97 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.15 to 0.4 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 to 0.0050 |
| Silicon (Si), % | 8.0 to 10 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0.5 to 1.5 |
| Residuals, % | 0 | |
| 0 to 0.3 |