355.0 Aluminum vs. 70Ag-30Ni Alloy
355.0 aluminum belongs to the aluminum alloys classification, while 70Ag-30Ni alloy belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 355.0 aluminum and the bottom bar is 70Ag-30Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 100 |
| Poisson's Ratio | 0.33 | |
| 0.35 |
| Shear Modulus, GPa | 27 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 260 | |
| 320 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 170 |
| Melting Completion (Liquidus), °C | 620 | |
| 960 |
| Melting Onset (Solidus), °C | 560 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 300 |
| Thermal Expansion, µm/m-K | 22 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 to 43 | |
| 69 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 to 140 | |
| 62 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 5.8 |
| Stiffness to Weight: Bending, points | 51 | |
| 16 |
| Strength to Weight: Axial, points | 20 to 27 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 28 to 33 | |
| 10 to 15 |
| Thermal Shock Resistance, points | 9.1 to 12 | |
| 13 to 21 |
Alloy Composition
| Aluminum (Al), % | 90.3 to 94.1 | |
| 0 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 1.0 to 1.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.6 | |
| 0 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 28.8 to 31 |
| Silicon (Si), % | 4.5 to 5.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 69 to 71 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |