355.0 Aluminum vs. EN 1.7383 Steel
355.0 aluminum belongs to the aluminum alloys classification, while EN 1.7383 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 355.0 aluminum and the bottom bar is EN 1.7383 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 72 to 83 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 190 |
| Elongation at Break, % | 1.5 to 2.6 | |
| 20 to 23 |
| Fatigue Strength, MPa | 55 to 70 | |
| 210 to 270 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 74 |
| Shear Strength, MPa | 150 to 240 | |
| 350 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 200 to 260 | |
| 560 to 610 |
| Tensile Strength: Yield (Proof), MPa | 150 to 190 | |
| 300 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 460 |
| Melting Completion (Liquidus), °C | 620 | |
| 1470 |
| Melting Onset (Solidus), °C | 560 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 470 |
| Thermal Conductivity, W/m-K | 150 to 170 | |
| 39 |
| Thermal Expansion, µm/m-K | 22 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 to 43 | |
| 7.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 to 140 | |
| 8.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 3.9 |
| Density, g/cm3 | 2.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 1.8 |
| Embodied Energy, MJ/kg | 150 | |
| 23 |
| Embodied Water, L/kg | 1120 | |
| 59 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.7 to 5.9 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 250 | |
| 240 to 420 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 27 | |
| 20 to 22 |
| Strength to Weight: Bending, points | 28 to 33 | |
| 19 to 20 |
| Thermal Diffusivity, mm2/s | 60 to 69 | |
| 11 |
| Thermal Shock Resistance, points | 9.1 to 12 | |
| 16 to 18 |
Alloy Composition
| Aluminum (Al), % | 90.3 to 94.1 | |
| 0 to 0.040 |
| Carbon (C), % | 0 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 0 to 0.25 | |
| 2.0 to 2.5 |
| Copper (Cu), % | 1.0 to 1.5 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.6 | |
| 94.3 to 96.6 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.4 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 4.5 to 5.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |