355.0 Aluminum vs. Low-oxygen Zirconium
355.0 aluminum belongs to the aluminum alloys classification, while low-oxygen zirconium belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 355.0 aluminum and the bottom bar is low-oxygen zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 71 | |
98 |
Elongation at Break, % | 1.5 to 2.6 | |
23 |
Poisson's Ratio | 0.33 | |
0.34 |
Shear Modulus, GPa | 27 | |
37 |
Tensile Strength: Ultimate (UTS), MPa | 200 to 260 | |
330 |
Tensile Strength: Yield (Proof), MPa | 150 to 190 | |
270 |
Thermal Properties
Latent Heat of Fusion, J/g | 470 | |
250 |
Specific Heat Capacity, J/kg-K | 890 | |
270 |
Thermal Conductivity, W/m-K | 150 to 170 | |
22 |
Thermal Expansion, µm/m-K | 22 | |
5.7 |
Otherwise Unclassified Properties
Density, g/cm3 | 2.7 | |
6.7 |
Embodied Water, L/kg | 1120 | |
450 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.7 to 5.9 | |
70 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 250 | |
370 |
Stiffness to Weight: Axial, points | 14 | |
8.1 |
Stiffness to Weight: Bending, points | 51 | |
23 |
Strength to Weight: Axial, points | 20 to 27 | |
14 |
Strength to Weight: Bending, points | 28 to 33 | |
16 |
Thermal Diffusivity, mm2/s | 60 to 69 | |
12 |
Thermal Shock Resistance, points | 9.1 to 12 | |
42 |
Alloy Composition
Aluminum (Al), % | 90.3 to 94.1 | |
0 |
Carbon (C), % | 0 | |
0 to 0.050 |
Chromium (Cr), % | 0 to 0.25 | |
0 to 0.2 |
Copper (Cu), % | 1.0 to 1.5 | |
0 |
Hafnium (Hf), % | 0 | |
0 to 4.5 |
Hydrogen (H), % | 0 | |
0 to 0.0050 |
Iron (Fe), % | 0 to 0.6 | |
0 to 0.2 |
Magnesium (Mg), % | 0.4 to 0.6 | |
0 |
Manganese (Mn), % | 0 to 0.5 | |
0 |
Nitrogen (N), % | 0 | |
0 to 0.025 |
Oxygen (O), % | 0 | |
0 to 0.1 |
Silicon (Si), % | 4.5 to 5.5 | |
0 |
Titanium (Ti), % | 0 to 0.25 | |
0 |
Zinc (Zn), % | 0 to 0.35 | |
0 |
Zirconium (Zr), % | 0 | |
94.7 to 100 |
Residuals, % | 0 to 0.15 | |
0 |