356.0 Aluminum vs. Ductile Cast Iron
356.0 aluminum belongs to the aluminum alloys classification, while ductile cast iron belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 356.0 aluminum and the bottom bar is ductile cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 to 75 | |
| 160 to 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 170 to 180 |
| Elongation at Break, % | 2.0 to 3.8 | |
| 2.1 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.28 to 0.31 |
| Shear Modulus, GPa | 27 | |
| 64 to 70 |
| Shear Strength, MPa | 140 to 190 | |
| 420 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 240 | |
| 460 to 920 |
| Tensile Strength: Yield (Proof), MPa | 100 to 190 | |
| 310 to 670 |
Thermal Properties
| Latent Heat of Fusion, J/g | 500 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 290 |
| Melting Completion (Liquidus), °C | 620 | |
| 1160 |
| Melting Onset (Solidus), °C | 570 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 490 |
| Thermal Conductivity, W/m-K | 150 to 170 | |
| 31 to 36 |
| Thermal Expansion, µm/m-K | 21 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 to 43 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 to 150 | |
| 8.8 to 9.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 1.9 |
| Density, g/cm3 | 2.6 | |
| 7.1 to 7.5 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 1.5 |
| Embodied Energy, MJ/kg | 150 | |
| 21 |
| Embodied Water, L/kg | 1110 | |
| 43 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.2 to 8.2 | |
| 17 to 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 70 to 250 | |
| 280 to 1330 |
| Stiffness to Weight: Axial, points | 15 | |
| 12 to 14 |
| Stiffness to Weight: Bending, points | 53 | |
| 24 to 26 |
| Strength to Weight: Axial, points | 17 to 26 | |
| 17 to 35 |
| Strength to Weight: Bending, points | 25 to 33 | |
| 18 to 29 |
| Thermal Diffusivity, mm2/s | 64 to 71 | |
| 8.9 to 10 |
| Thermal Shock Resistance, points | 7.6 to 11 | |
| 17 to 35 |
Alloy Composition
| Aluminum (Al), % | 90.1 to 93.3 | |
| 0 |
| Carbon (C), % | 0 | |
| 3.0 to 3.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 0 to 0.6 | |
| 93.7 to 95.5 |
| Magnesium (Mg), % | 0.2 to 0.45 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.080 |
| Silicon (Si), % | 6.5 to 7.5 | |
| 1.5 to 2.8 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 |
| Zinc (Zn), % | 0 to 0.35 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |