356.0 Aluminum vs. EN AC-44300 Aluminum
Both 356.0 aluminum and EN AC-44300 aluminum are aluminum alloys. They have a moderately high 95% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 356.0 aluminum and the bottom bar is EN AC-44300 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 to 75 | |
| 68 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 72 |
| Elongation at Break, % | 2.0 to 3.8 | |
| 1.1 |
| Fatigue Strength, MPa | 55 to 75 | |
| 100 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 27 | |
| 27 |
| Tensile Strength: Ultimate (UTS), MPa | 160 to 240 | |
| 270 |
| Tensile Strength: Yield (Proof), MPa | 100 to 190 | |
| 150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 500 | |
| 570 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 620 | |
| 590 |
| Melting Onset (Solidus), °C | 570 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 150 to 170 | |
| 130 |
| Thermal Expansion, µm/m-K | 21 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 to 43 | |
| 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 to 150 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.6 | |
| 2.5 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 7.7 |
| Embodied Energy, MJ/kg | 150 | |
| 140 |
| Embodied Water, L/kg | 1110 | |
| 1050 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 3.2 to 8.2 | |
| 2.6 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 70 to 250 | |
| 150 |
| Stiffness to Weight: Axial, points | 15 | |
| 16 |
| Stiffness to Weight: Bending, points | 53 | |
| 55 |
| Strength to Weight: Axial, points | 17 to 26 | |
| 29 |
| Strength to Weight: Bending, points | 25 to 33 | |
| 36 |
| Thermal Diffusivity, mm2/s | 64 to 71 | |
| 58 |
| Thermal Shock Resistance, points | 7.6 to 11 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 90.1 to 93.3 | |
| 84.3 to 89.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.6 | |
| 0 to 1.0 |
| Magnesium (Mg), % | 0.2 to 0.45 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.55 |
| Silicon (Si), % | 6.5 to 7.5 | |
| 10.5 to 13.5 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 to 0.35 | |
| 0 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.25 |