359.0 Aluminum vs. R31233 Cobalt
359.0 aluminum belongs to the aluminum alloys classification, while R31233 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is 359.0 aluminum and the bottom bar is R31233 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 220 |
| Elongation at Break, % | 3.8 to 4.9 | |
| 17 |
| Fatigue Strength, MPa | 100 | |
| 220 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 85 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 350 | |
| 1020 |
| Tensile Strength: Yield (Proof), MPa | 250 to 280 | |
| 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 530 | |
| 320 |
| Melting Completion (Liquidus), °C | 600 | |
| 1350 |
| Melting Onset (Solidus), °C | 570 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 910 | |
| 440 |
| Thermal Conductivity, W/m-K | 140 | |
| 12 |
| Thermal Expansion, µm/m-K | 21 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 2.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.6 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.4 |
| Embodied Energy, MJ/kg | 150 | |
| 110 |
| Embodied Water, L/kg | 1090 | |
| 480 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 12 to 15 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 450 to 540 | |
| 410 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 54 | |
| 23 |
| Strength to Weight: Axial, points | 37 to 38 | |
| 33 |
| Strength to Weight: Bending, points | 42 to 43 | |
| 26 |
| Thermal Diffusivity, mm2/s | 59 | |
| 3.2 |
| Thermal Shock Resistance, points | 16 to 17 | |
| 25 |
Alloy Composition
| Aluminum (Al), % | 88.9 to 91 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 0 | |
| 23.5 to 27.5 |
| Cobalt (Co), % | 0 | |
| 44.7 to 63.3 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 1.0 to 5.0 |
| Magnesium (Mg), % | 0.5 to 0.7 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.1 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 0 | |
| 7.0 to 11 |
| Nitrogen (N), % | 0 | |
| 0.030 to 0.12 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 8.5 to 9.5 | |
| 0.050 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 |
| Tungsten (W), % | 0 | |
| 1.0 to 3.0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |