5010-F Aluminum vs. ISO-WD32350-F
5010-F aluminum belongs to the aluminum alloys classification, while ISO-WD32350-F belongs to the magnesium alloys.
For each property being compared, the top bar is 5010-F aluminum and the bottom bar is ISO-WD32350-F.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 45 |
| Elongation at Break, % | 23 | |
| 10 |
| Fatigue Strength, MPa | 35 | |
| 120 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 64 | |
| 150 |
| Tensile Strength: Ultimate (UTS), MPa | 100 | |
| 260 |
| Tensile Strength: Yield (Proof), MPa | 38 | |
| 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 340 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 95 |
| Melting Completion (Liquidus), °C | 650 | |
| 600 |
| Melting Onset (Solidus), °C | 630 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 990 |
| Thermal Conductivity, W/m-K | 200 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 25 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 45 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 150 | |
| 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1190 | |
| 960 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 19 | |
| 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 10 | |
| 310 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 68 |
| Strength to Weight: Axial, points | 10 | |
| 42 |
| Strength to Weight: Bending, points | 18 | |
| 52 |
| Thermal Diffusivity, mm2/s | 82 | |
| 73 |
| Thermal Shock Resistance, points | 4.5 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 97.1 to 99.7 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 to 0.15 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 to 0.060 |
| Magnesium (Mg), % | 0.2 to 0.6 | |
| 95.7 to 97.7 |
| Manganese (Mn), % | 0.1 to 0.3 | |
| 0.6 to 1.3 |
| Nickel (Ni), % | 0 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.1 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.3 | |
| 1.8 to 2.3 |
| Residuals, % | 0 | |
| 0 to 0.3 |