5026-H34 Aluminum vs. 6025-H34 Aluminum
Both 5026-H34 aluminum and 6025-H34 aluminum are aluminum alloys. Both are furnished in the H34 temper. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is 5026-H34 aluminum and the bottom bar is 6025-H34 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 70 |
| Elongation at Break, % | 11 | |
| 2.8 |
| Fatigue Strength, MPa | 140 | |
| 99 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 160 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 160 |
| Melting Completion (Liquidus), °C | 650 | |
| 650 |
| Melting Onset (Solidus), °C | 510 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 130 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 31 | |
| 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.8 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 8.9 | |
| 8.5 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1150 | |
| 1160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 29 | |
| 6.0 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 250 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 49 | |
| 50 |
| Strength to Weight: Axial, points | 27 | |
| 23 |
| Strength to Weight: Bending, points | 34 | |
| 30 |
| Thermal Diffusivity, mm2/s | 52 | |
| 54 |
| Thermal Shock Resistance, points | 12 | |
| 10 |
Alloy Composition
| Aluminum (Al), % | 88.2 to 94.7 | |
| 91.7 to 96.3 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 to 0.2 |
| Copper (Cu), % | 0.1 to 0.8 | |
| 0.2 to 0.7 |
| Iron (Fe), % | 0.2 to 1.0 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 3.9 to 4.9 | |
| 2.1 to 3.0 |
| Manganese (Mn), % | 0.6 to 1.8 | |
| 0.6 to 1.4 |
| Silicon (Si), % | 0.55 to 1.4 | |
| 0.8 to 1.5 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 to 0.5 |
| Zirconium (Zr), % | 0 to 0.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |