5059 Aluminum vs. Grade 5 Titanium
5059 aluminum belongs to the aluminum alloys classification, while grade 5 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 5059 aluminum and the bottom bar is grade 5 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 110 |
| Elongation at Break, % | 11 to 25 | |
| 8.6 to 11 |
| Fatigue Strength, MPa | 170 to 240 | |
| 530 to 630 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 40 |
| Shear Strength, MPa | 220 to 250 | |
| 600 to 710 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 410 | |
| 1000 to 1190 |
| Tensile Strength: Yield (Proof), MPa | 170 to 300 | |
| 910 to 1110 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 330 |
| Melting Completion (Liquidus), °C | 650 | |
| 1610 |
| Melting Onset (Solidus), °C | 510 | |
| 1650 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 560 |
| Thermal Conductivity, W/m-K | 110 | |
| 6.8 |
| Thermal Expansion, µm/m-K | 24 | |
| 8.9 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 95 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 36 |
| Density, g/cm3 | 2.7 | |
| 4.4 |
| Embodied Carbon, kg CO2/kg material | 9.1 | |
| 38 |
| Embodied Energy, MJ/kg | 160 | |
| 610 |
| Embodied Water, L/kg | 1160 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 42 to 75 | |
| 100 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 to 650 | |
| 3980 to 5880 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 50 | |
| 35 |
| Strength to Weight: Axial, points | 36 to 42 | |
| 62 to 75 |
| Strength to Weight: Bending, points | 41 to 45 | |
| 50 to 56 |
| Thermal Diffusivity, mm2/s | 44 | |
| 2.7 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 76 to 91 |
Alloy Composition
| Aluminum (Al), % | 89.9 to 94 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 to 0.25 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 5.0 to 6.0 | |
| 0 |
| Manganese (Mn), % | 0.6 to 1.2 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.45 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 87.4 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Yttrium (Y), % | 0 | |
| 0 to 0.0050 |
| Zinc (Zn), % | 0.4 to 0.9 | |
| 0 |
| Zirconium (Zr), % | 0.050 to 0.25 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |