50Cr-50Ni Alloy vs. C61400 Bronze
50Cr-50Ni alloy belongs to the otherwise unclassified metals classification, while C61400 bronze belongs to the copper alloys. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is 50Cr-50Ni alloy and the bottom bar is C61400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 5.7 | |
| 34 to 40 |
| Poisson's Ratio | 0.26 | |
| 0.34 |
| Shear Modulus, GPa | 84 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 540 to 570 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 220 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 420 |
| Thermal Expansion, µm/m-K | 15 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 50 | |
| 28 |
| Density, g/cm3 | 8.0 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 3.0 |
| Embodied Energy, MJ/kg | 110 | |
| 48 |
| Embodied Water, L/kg | 350 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 | |
| 160 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 350 | |
| 210 to 310 |
| Stiffness to Weight: Axial, points | 15 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 21 | |
| 18 to 19 |
| Strength to Weight: Bending, points | 20 | |
| 17 to 18 |
| Thermal Shock Resistance, points | 14 | |
| 18 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.25 | |
| 6.0 to 8.0 |
| Carbon (C), % | 0 to 0.1 | |
| 0 |
| Chromium (Cr), % | 48 to 52 | |
| 0 |
| Copper (Cu), % | 0 | |
| 86 to 92.5 |
| Iron (Fe), % | 0 to 1.0 | |
| 1.5 to 3.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 to 1.0 |
| Nickel (Ni), % | 44.5 to 52 | |
| 0 |
| Nitrogen (N), % | 0 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 |
| Titanium (Ti), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |