512.0 Aluminum vs. N10629 Nickel

512.0 aluminum belongs to the aluminum alloys classification, while N10629 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 512.0 aluminum and the bottom bar is N10629 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 69
220
Elongation at Break, % 2.0
45
Fatigue Strength, MPa 58
340
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 26
83
Tensile Strength: Ultimate (UTS), MPa 130
860
Tensile Strength: Yield (Proof), MPa 83
400

Thermal Properties

Latent Heat of Fusion, J/g 420
310
Maximum Temperature: Mechanical, °C 180
910
Melting Completion (Liquidus), °C 630
1610
Melting Onset (Solidus), °C 590
1560
Specific Heat Capacity, J/kg-K 900
390
Thermal Expansion, µm/m-K 23
10

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
75
Density, g/cm3 2.7
9.2
Embodied Carbon, kg CO2/kg material 8.8
15
Embodied Energy, MJ/kg 150
190
Embodied Water, L/kg 1160
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 2.3
320
Resilience: Unit (Modulus of Resilience), kJ/m3 50
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 51
22
Strength to Weight: Axial, points 14
26
Strength to Weight: Bending, points 22
22
Thermal Shock Resistance, points 6.1
27

Alloy Composition

Aluminum (Al), % 90.6 to 95.1
0.1 to 0.5
Carbon (C), % 0
0 to 0.010
Chromium (Cr), % 0 to 0.25
0.5 to 1.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0 to 0.35
0 to 0.5
Iron (Fe), % 0 to 0.6
1.0 to 6.0
Magnesium (Mg), % 3.5 to 4.5
0
Manganese (Mn), % 0 to 0.8
0 to 1.5
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0
65 to 72.4
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 1.4 to 2.2
0 to 0.050
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0 to 0.25
0
Zinc (Zn), % 0 to 0.35
0
Residuals, % 0 to 0.15
0