513.0 Aluminum vs. 1080A Aluminum
Both 513.0 aluminum and 1080A aluminum are aluminum alloys. They have a moderately high 94% of their average alloy composition in common.
For each property being compared, the top bar is 513.0 aluminum and the bottom bar is 1080A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 55 | |
| 18 to 40 |
| Elastic (Young's, Tensile) Modulus, GPa | 68 | |
| 68 |
| Elongation at Break, % | 5.7 | |
| 2.3 to 34 |
| Fatigue Strength, MPa | 97 | |
| 18 to 50 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 170 | |
| 49 to 81 |
| Tensile Strength: Ultimate (UTS), MPa | 200 | |
| 74 to 140 |
| Tensile Strength: Yield (Proof), MPa | 120 | |
| 17 to 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 170 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 590 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 130 | |
| 230 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 62 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 200 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.7 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.8 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1170 | |
| 1200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 9.8 | |
| 3.1 to 19 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 | |
| 2.1 to 100 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 20 | |
| 7.6 to 15 |
| Strength to Weight: Bending, points | 28 | |
| 14 to 22 |
| Thermal Diffusivity, mm2/s | 54 | |
| 94 |
| Thermal Shock Resistance, points | 8.8 | |
| 3.3 to 6.4 |
Alloy Composition
| Aluminum (Al), % | 91.9 to 95.1 | |
| 99.8 to 100 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.030 |
| Gallium (Ga), % | 0 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 3.5 to 4.5 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0 to 0.3 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.15 |
| Titanium (Ti), % | 0 to 0.2 | |
| 0 to 0.020 |
| Zinc (Zn), % | 1.4 to 2.2 | |
| 0 to 0.060 |
| Residuals, % | 0 to 0.15 | |
| 0 |