515.0 Aluminum vs. 2017A Aluminum
Both 515.0 aluminum and 2017A aluminum are aluminum alloys. They have a very high 96% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is 515.0 aluminum and the bottom bar is 2017A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 10 | |
| 2.2 to 14 |
| Fatigue Strength, MPa | 130 | |
| 92 to 130 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 190 | |
| 120 to 270 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 200 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 220 |
| Melting Completion (Liquidus), °C | 620 | |
| 650 |
| Melting Onset (Solidus), °C | 620 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 880 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 11 |
| Density, g/cm3 | 2.6 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.2 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1120 | |
| 1140 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 52 | |
| 46 |
| Strength to Weight: Axial, points | 30 | |
| 19 to 42 |
| Strength to Weight: Bending, points | 36 | |
| 26 to 44 |
| Thermal Shock Resistance, points | 13 | |
| 8.9 to 20 |
Alloy Composition
| Aluminum (Al), % | 93.6 to 96.6 | |
| 91.3 to 95.5 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.2 | |
| 3.5 to 4.5 |
| Iron (Fe), % | 0 to 1.3 | |
| 0 to 0.7 |
| Magnesium (Mg), % | 2.5 to 4.0 | |
| 0.4 to 1.0 |
| Manganese (Mn), % | 0.4 to 0.6 | |
| 0.4 to 1.0 |
| Silicon (Si), % | 0.5 to 10 | |
| 0.2 to 0.8 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |