518.0 Aluminum vs. EN-MC21120 Magnesium
518.0 aluminum belongs to the aluminum alloys classification, while EN-MC21120 magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 518.0 aluminum and the bottom bar is EN-MC21120 magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 80 | |
| 63 to 75 |
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 46 |
| Elongation at Break, % | 5.0 | |
| 2.2 to 6.7 |
| Fatigue Strength, MPa | 140 | |
| 84 to 96 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 25 | |
| 18 |
| Shear Strength, MPa | 200 | |
| 110 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 200 to 270 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 130 to 170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 130 |
| Melting Completion (Liquidus), °C | 620 | |
| 600 |
| Melting Onset (Solidus), °C | 560 | |
| 490 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 990 |
| Thermal Conductivity, W/m-K | 98 | |
| 76 |
| Thermal Expansion, µm/m-K | 24 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 81 | |
| 59 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.7 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 9.4 | |
| 22 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1160 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 | |
| 5.0 to 15 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 | |
| 180 to 320 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 51 | |
| 69 |
| Strength to Weight: Axial, points | 32 | |
| 31 to 43 |
| Strength to Weight: Bending, points | 38 | |
| 43 to 53 |
| Thermal Diffusivity, mm2/s | 40 | |
| 44 |
| Thermal Shock Resistance, points | 14 | |
| 11 to 16 |
Alloy Composition
| Aluminum (Al), % | 88.1 to 92.5 | |
| 8.3 to 9.7 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.030 |
| Iron (Fe), % | 0 to 1.8 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 7.5 to 8.5 | |
| 88.6 to 91.3 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.1 to 0.5 |
| Nickel (Ni), % | 0 to 0.15 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.15 | |
| 0.35 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.010 |