535.0 Aluminum vs. EN 1.4835 Stainless Steel

535.0 aluminum belongs to the aluminum alloys classification, while EN 1.4835 stainless steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 535.0 aluminum and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 70
180
Elastic (Young's, Tensile) Modulus, GPa 67
200
Elongation at Break, % 10
43
Fatigue Strength, MPa 70
310
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 25
77
Shear Strength, MPa 190
520
Tensile Strength: Ultimate (UTS), MPa 270
750
Tensile Strength: Yield (Proof), MPa 140
350

Thermal Properties

Latent Heat of Fusion, J/g 390
320
Maximum Temperature: Mechanical, °C 170
1150
Melting Completion (Liquidus), °C 630
1400
Melting Onset (Solidus), °C 570
1360
Specific Heat Capacity, J/kg-K 910
490
Thermal Conductivity, W/m-K 100
15
Thermal Expansion, µm/m-K 24
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 23
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 79
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
17
Density, g/cm3 2.6
7.7
Embodied Carbon, kg CO2/kg material 9.4
3.3
Embodied Energy, MJ/kg 160
47
Embodied Water, L/kg 1180
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 24
270
Resilience: Unit (Modulus of Resilience), kJ/m3 150
310
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 51
25
Strength to Weight: Axial, points 28
27
Strength to Weight: Bending, points 35
24
Thermal Diffusivity, mm2/s 42
4.0
Thermal Shock Resistance, points 12
16

Alloy Composition

Aluminum (Al), % 91.5 to 93.6
0
Beryllium (Be), % 0.0030 to 0.0070
0
Boron (B), % 0 to 0.0050
0
Carbon (C), % 0
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 0
20 to 22
Copper (Cu), % 0 to 0.050
0
Iron (Fe), % 0 to 0.15
62 to 68.4
Magnesium (Mg), % 6.2 to 7.5
0
Manganese (Mn), % 0.1 to 0.25
0 to 1.0
Nickel (Ni), % 0
10 to 12
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0
0 to 0.045
Silicon (Si), % 0 to 0.15
1.4 to 2.5
Sulfur (S), % 0
0 to 0.015
Titanium (Ti), % 0.1 to 0.25
0
Residuals, % 0 to 0.15
0