6013 Aluminum vs. Grade 9 Titanium
6013 aluminum belongs to the aluminum alloys classification, while grade 9 titanium belongs to the titanium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 6013 aluminum and the bottom bar is grade 9 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 110 |
| Elongation at Break, % | 3.4 to 22 | |
| 11 to 17 |
| Fatigue Strength, MPa | 98 to 140 | |
| 330 to 480 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 40 |
| Shear Strength, MPa | 190 to 240 | |
| 430 to 580 |
| Tensile Strength: Ultimate (UTS), MPa | 310 to 410 | |
| 700 to 960 |
| Tensile Strength: Yield (Proof), MPa | 170 to 350 | |
| 540 to 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 410 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 330 |
| Melting Completion (Liquidus), °C | 650 | |
| 1640 |
| Melting Onset (Solidus), °C | 580 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 550 |
| Thermal Conductivity, W/m-K | 150 | |
| 8.1 |
| Thermal Expansion, µm/m-K | 23 | |
| 9.1 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 37 |
| Density, g/cm3 | 2.8 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 8.3 | |
| 36 |
| Embodied Energy, MJ/kg | 150 | |
| 580 |
| Embodied Water, L/kg | 1170 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 58 | |
| 89 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 900 | |
| 1380 to 3220 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 49 | |
| 35 |
| Strength to Weight: Axial, points | 31 to 41 | |
| 43 to 60 |
| Strength to Weight: Bending, points | 37 to 44 | |
| 39 to 48 |
| Thermal Diffusivity, mm2/s | 60 | |
| 3.3 |
| Thermal Shock Resistance, points | 14 to 18 | |
| 52 to 71 |
Alloy Composition
| Aluminum (Al), % | 94.8 to 97.8 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0.6 to 1.1 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0.8 to 1.2 | |
| 0 |
| Manganese (Mn), % | 0.2 to 0.8 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Silicon (Si), % | 0.6 to 1.0 | |
| 0 |
| Titanium (Ti), % | 0 to 0.1 | |
| 92.6 to 95.5 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |