60Cr-40Ni Alloy vs. SAE-AISI M6 Steel

60Cr-40Ni alloy belongs to the otherwise unclassified metals classification, while SAE-AISI M6 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is 60Cr-40Ni alloy and the bottom bar is SAE-AISI M6 steel.

60Cr-40Ni (R20600) Casting Alloy SAE-AISI M6 (T11306) Cobalt High-Speed Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		200

Poisson's Ratio		0.25
Poisson's Ratio		0.29

Shear Modulus, GPa		87
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		870
Tensile Strength: Ultimate (UTS), MPa		840 to 2210

Thermal Properties

Latent Heat of Fusion, J/g		370
Latent Heat of Fusion, J/g		260

Specific Heat Capacity, J/kg-K		490
Specific Heat Capacity, J/kg-K		440

Thermal Expansion, µm/m-K		16
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		49
Base Metal Price, % relative		39

Density, g/cm³		7.8
Density, g/cm³		8.4

Embodied Carbon, kg CO₂/kg material		7.4
Embodied Carbon, kg CO₂/kg material		8.0

Embodied Energy, MJ/kg		110
Embodied Energy, MJ/kg		120

Embodied Water, L/kg		380
Embodied Water, L/kg		160

Common Calculations

Stiffness to Weight: Axial, points		16
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		26
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		31
Strength to Weight: Axial, points		28 to 73

Strength to Weight: Bending, points		26
Strength to Weight: Bending, points		24 to 45

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		26 to 68

Alloy Composition

Aluminum (Al), %		0 to 0.25
Aluminum (Al), %		0

Carbon (C), %		0 to 0.1
Carbon (C), %		0.75 to 0.85

Chromium (Cr), %		58 to 62
Chromium (Cr), %		3.8 to 4.5

Cobalt (Co), %		0
Cobalt (Co), %		11 to 13

Iron (Fe), %		0 to 1.0
Iron (Fe), %		68.8 to 74.6

Manganese (Mn), %		0 to 0.3
Manganese (Mn), %		0.15 to 0.4

Molybdenum (Mo), %		0
Molybdenum (Mo), %		4.5 to 5.5

Nickel (Ni), %		34.5 to 42
Nickel (Ni), %		0

Nitrogen (N), %		0 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.2 to 0.45

Sulfur (S), %		0 to 0.020
Sulfur (S), %		0 to 0.030

Titanium (Ti), %		0 to 0.5
Titanium (Ti), %		0

Tungsten (W), %		0
Tungsten (W), %		3.8 to 4.8

Vanadium (V), %		0
Vanadium (V), %		1.3 to 1.7