705.0 Aluminum vs. 5154 Aluminum
Both 705.0 aluminum and 5154 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is 705.0 aluminum and the bottom bar is 5154 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 68 |
| Elongation at Break, % | 8.4 to 10 | |
| 3.4 to 20 |
| Fatigue Strength, MPa | 63 to 98 | |
| 100 to 160 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 260 | |
| 240 to 360 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 94 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 190 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 610 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 890 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 34 | |
| 32 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.8 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1170 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 20 | |
| 11 to 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 130 | |
| 64 to 540 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 49 | |
| 51 |
| Strength to Weight: Axial, points | 24 to 26 | |
| 25 to 37 |
| Strength to Weight: Bending, points | 31 to 32 | |
| 32 to 42 |
| Thermal Diffusivity, mm2/s | 55 | |
| 52 |
| Thermal Shock Resistance, points | 11 | |
| 10 to 16 |
Alloy Composition
| Aluminum (Al), % | 92.3 to 98.6 | |
| 94.4 to 96.8 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0.15 to 0.35 |
| Copper (Cu), % | 0 to 0.2 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.4 |
| Magnesium (Mg), % | 1.4 to 1.8 | |
| 3.1 to 3.9 |
| Manganese (Mn), % | 0 to 0.6 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.2 | |
| 0 to 0.25 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 3.3 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |