710.0-F Aluminum vs. 713.0-F Aluminum
Both 710.0-F aluminum and 713.0-F aluminum are aluminum alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is 710.0-F aluminum and the bottom bar is 713.0-F aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 75 | |
74 |
Elastic (Young's, Tensile) Modulus, GPa | 70 | |
71 |
Elongation at Break, % | 3.6 | |
4.2 |
Fatigue Strength, MPa | 55 | |
63 |
Poisson's Ratio | 0.32 | |
0.32 |
Shear Modulus, GPa | 26 | |
27 |
Shear Strength, MPa | 180 | |
180 |
Tensile Strength: Ultimate (UTS), MPa | 240 | |
240 |
Tensile Strength: Yield (Proof), MPa | 160 | |
170 |
Thermal Properties
Latent Heat of Fusion, J/g | 380 | |
370 |
Maximum Temperature: Mechanical, °C | 170 | |
180 |
Melting Completion (Liquidus), °C | 650 | |
630 |
Melting Onset (Solidus), °C | 610 | |
610 |
Solidification (Pattern Maker's) Shrinkage, % | 1.6 | |
1.6 |
Specific Heat Capacity, J/kg-K | 870 | |
860 |
Thermal Conductivity, W/m-K | 140 | |
150 |
Thermal Expansion, µm/m-K | 24 | |
24 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 35 | |
35 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
100 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 9.5 | |
9.5 |
Density, g/cm3 | 3.0 | |
3.1 |
Embodied Carbon, kg CO2/kg material | 8.0 | |
7.8 |
Embodied Energy, MJ/kg | 150 | |
150 |
Embodied Water, L/kg | 1130 | |
1110 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.9 | |
9.2 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
210 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 46 | |
45 |
Strength to Weight: Axial, points | 23 | |
22 |
Strength to Weight: Bending, points | 29 | |
28 |
Thermal Diffusivity, mm2/s | 53 | |
57 |
Thermal Shock Resistance, points | 10 | |
10 |
Alloy Composition
Aluminum (Al), % | 90.5 to 93.1 | |
87.6 to 92.4 |
Chromium (Cr), % | 0 | |
0 to 0.35 |
Copper (Cu), % | 0.35 to 0.65 | |
0.4 to 1.0 |
Iron (Fe), % | 0 to 0.5 | |
0 to 1.1 |
Magnesium (Mg), % | 0.6 to 0.8 | |
0.2 to 0.5 |
Manganese (Mn), % | 0 to 0.050 | |
0 to 0.6 |
Nickel (Ni), % | 0 | |
0 to 0.15 |
Silicon (Si), % | 0 to 0.15 | |
0 to 0.25 |
Titanium (Ti), % | 0 to 0.25 | |
0 to 0.25 |
Zinc (Zn), % | 6.0 to 7.0 | |
7.0 to 8.0 |
Residuals, % | 0 | |
0 to 0.25 |