710.0 Aluminum vs. 4045 Aluminum
Both 710.0 aluminum and 4045 aluminum are aluminum alloys. They have 90% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 710.0 aluminum and the bottom bar is 4045 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 71 |
| Elongation at Break, % | 2.2 to 3.6 | |
| 2.3 |
| Fatigue Strength, MPa | 55 to 110 | |
| 45 |
| Poisson's Ratio | 0.32 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 27 |
| Shear Strength, MPa | 180 | |
| 69 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 250 | |
| 120 |
| Tensile Strength: Yield (Proof), MPa | 160 | |
| 64 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 540 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 650 | |
| 600 |
| Melting Onset (Solidus), °C | 610 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 900 |
| Thermal Conductivity, W/m-K | 140 | |
| 170 |
| Thermal Expansion, µm/m-K | 24 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 110 | |
| 160 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 3.0 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 7.8 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1130 | |
| 1070 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.9 to 7.9 | |
| 2.4 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 190 | |
| 29 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 46 | |
| 54 |
| Strength to Weight: Axial, points | 23 | |
| 13 |
| Strength to Weight: Bending, points | 29 | |
| 21 |
| Thermal Diffusivity, mm2/s | 53 | |
| 74 |
| Thermal Shock Resistance, points | 10 to 11 | |
| 5.7 |
Alloy Composition
| Aluminum (Al), % | 90.5 to 93.1 | |
| 87.4 to 91 |
| Copper (Cu), % | 0.35 to 0.65 | |
| 0 to 0.3 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.8 |
| Magnesium (Mg), % | 0.6 to 0.8 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0 to 0.050 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.15 | |
| 9.0 to 11 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.2 |
| Zinc (Zn), % | 6.0 to 7.0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.15 |