712.0 Aluminum vs. 7075 Aluminum
Both 712.0 aluminum and 7075 aluminum are aluminum alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is 712.0 aluminum and the bottom bar is 7075 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 70 |
| Elongation at Break, % | 4.5 to 4.7 | |
| 1.8 to 12 |
| Fatigue Strength, MPa | 140 to 180 | |
| 110 to 190 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 180 | |
| 150 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 260 | |
| 240 to 590 |
| Tensile Strength: Yield (Proof), MPa | 180 to 200 | |
| 120 to 510 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 200 |
| Melting Completion (Liquidus), °C | 640 | |
| 640 |
| Melting Onset (Solidus), °C | 610 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 870 |
| Thermal Conductivity, W/m-K | 160 | |
| 130 |
| Thermal Expansion, µm/m-K | 24 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 40 | |
| 33 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 120 | |
| 98 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 10 |
| Density, g/cm3 | 3.0 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1140 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 | |
| 7.8 to 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 270 | |
| 110 to 1870 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 46 |
| Strength to Weight: Axial, points | 24 to 25 | |
| 22 to 54 |
| Strength to Weight: Bending, points | 30 to 31 | |
| 28 to 52 |
| Thermal Diffusivity, mm2/s | 62 | |
| 50 |
| Thermal Shock Resistance, points | 11 | |
| 10 to 25 |
Alloy Composition
| Aluminum (Al), % | 90.7 to 94 | |
| 86.9 to 91.4 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 0.18 to 0.28 |
| Copper (Cu), % | 0 to 0.25 | |
| 1.2 to 2.0 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0.5 to 0.65 | |
| 2.1 to 2.9 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.4 |
| Titanium (Ti), % | 0.15 to 0.25 | |
| 0 to 0.2 |
| Zinc (Zn), % | 5.0 to 6.5 | |
| 5.1 to 6.1 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |