772.0 Aluminum vs. Grade 19 Titanium
772.0 aluminum belongs to the aluminum alloys classification, while grade 19 titanium belongs to the titanium alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is 772.0 aluminum and the bottom bar is grade 19 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 69 | |
| 120 |
| Elongation at Break, % | 6.3 to 8.4 | |
| 5.6 to 17 |
| Fatigue Strength, MPa | 94 to 160 | |
| 550 to 620 |
| Poisson's Ratio | 0.32 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 47 |
| Tensile Strength: Ultimate (UTS), MPa | 260 to 320 | |
| 890 to 1300 |
| Tensile Strength: Yield (Proof), MPa | 220 to 250 | |
| 870 to 1170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 380 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 370 |
| Melting Completion (Liquidus), °C | 630 | |
| 1660 |
| Melting Onset (Solidus), °C | 580 | |
| 1600 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 520 |
| Thermal Conductivity, W/m-K | 150 | |
| 6.2 |
| Thermal Expansion, µm/m-K | 24 | |
| 9.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 45 |
| Density, g/cm3 | 3.0 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 47 |
| Embodied Energy, MJ/kg | 150 | |
| 760 |
| Embodied Water, L/kg | 1140 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 25 | |
| 70 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 350 to 430 | |
| 3040 to 5530 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 46 | |
| 33 |
| Strength to Weight: Axial, points | 25 to 31 | |
| 49 to 72 |
| Strength to Weight: Bending, points | 31 to 36 | |
| 41 to 53 |
| Thermal Diffusivity, mm2/s | 58 | |
| 2.4 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 57 to 83 |
Alloy Composition
| Aluminum (Al), % | 91.2 to 93.2 | |
| 3.0 to 4.0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0.060 to 0.2 | |
| 5.5 to 6.5 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.020 |
| Iron (Fe), % | 0 to 0.15 | |
| 0 to 0.3 |
| Magnesium (Mg), % | 0.6 to 0.8 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.12 |
| Silicon (Si), % | 0 to 0.15 | |
| 0 |
| Titanium (Ti), % | 0.1 to 0.2 | |
| 71.1 to 77 |
| Vanadium (V), % | 0 | |
| 7.5 to 8.5 |
| Zinc (Zn), % | 6.0 to 7.0 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 3.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |