852.0 Aluminum vs. CR014A Copper

852.0 aluminum belongs to the aluminum alloys classification, while CR014A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is 852.0 aluminum and the bottom bar is CR014A copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
120
Elongation at Break, % 3.4
15
Poisson's Ratio 0.33
0.34
Shear Modulus, GPa 26
43
Tensile Strength: Ultimate (UTS), MPa 200
230
Tensile Strength: Yield (Proof), MPa 150
140

Thermal Properties

Latent Heat of Fusion, J/g 370
210
Maximum Temperature: Mechanical, °C 190
200
Melting Completion (Liquidus), °C 640
1090
Melting Onset (Solidus), °C 210
1040
Specific Heat Capacity, J/kg-K 840
390
Thermal Conductivity, W/m-K 180
380
Thermal Expansion, µm/m-K 23
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 45
98
Electrical Conductivity: Equal Weight (Specific), % IACS 130
99

Otherwise Unclassified Properties

Base Metal Price, % relative 15
32
Density, g/cm3 3.2
9.0
Embodied Carbon, kg CO2/kg material 8.5
2.6
Embodied Energy, MJ/kg 160
42
Embodied Water, L/kg 1150
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 6.2
31
Resilience: Unit (Modulus of Resilience), kJ/m3 160
83
Stiffness to Weight: Axial, points 12
7.2
Stiffness to Weight: Bending, points 43
18
Strength to Weight: Axial, points 17
7.1
Strength to Weight: Bending, points 24
9.3
Thermal Diffusivity, mm2/s 65
110
Thermal Shock Resistance, points 8.7
8.1

Alloy Composition

Aluminum (Al), % 86.6 to 91.3
0
Bismuth (Bi), % 0
0 to 0.00050
Copper (Cu), % 1.7 to 2.3
99.913 to 99.969
Iron (Fe), % 0 to 0.7
0
Magnesium (Mg), % 0.6 to 0.9
0
Manganese (Mn), % 0 to 0.1
0
Nickel (Ni), % 0.9 to 1.5
0
Phosphorus (P), % 0
0.0010 to 0.0070
Silicon (Si), % 0 to 0.4
0
Silver (Ag), % 0
0.030 to 0.050
Tin (Sn), % 5.5 to 7.0
0
Titanium (Ti), % 0 to 0.2
0
Residuals, % 0 to 0.3
0