A206.0 Aluminum vs. C69700 Brass
A206.0 aluminum belongs to the aluminum alloys classification, while C69700 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is A206.0 aluminum and the bottom bar is C69700 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 110 |
| Elongation at Break, % | 4.2 to 10 | |
| 25 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 41 |
| Shear Strength, MPa | 260 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 440 | |
| 470 |
| Tensile Strength: Yield (Proof), MPa | 250 to 380 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 390 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 160 |
| Melting Completion (Liquidus), °C | 670 | |
| 930 |
| Melting Onset (Solidus), °C | 550 | |
| 880 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 400 |
| Thermal Conductivity, W/m-K | 130 | |
| 43 |
| Thermal Expansion, µm/m-K | 23 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 26 |
| Density, g/cm3 | 3.0 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 2.7 |
| Embodied Energy, MJ/kg | 150 | |
| 44 |
| Embodied Water, L/kg | 1150 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 37 | |
| 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 to 1000 | |
| 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 46 | |
| 19 |
| Strength to Weight: Axial, points | 36 to 41 | |
| 16 |
| Strength to Weight: Bending, points | 39 to 43 | |
| 16 |
| Thermal Diffusivity, mm2/s | 48 | |
| 13 |
| Thermal Shock Resistance, points | 17 to 19 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 93.9 to 95.7 | |
| 0 |
| Copper (Cu), % | 4.2 to 5.0 | |
| 75 to 80 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0.5 to 1.5 |
| Magnesium (Mg), % | 0 to 0.15 | |
| 0 |
| Manganese (Mn), % | 0 to 0.2 | |
| 0 to 0.4 |
| Nickel (Ni), % | 0 to 0.050 | |
| 0 |
| Silicon (Si), % | 0 to 0.050 | |
| 2.5 to 3.5 |
| Tin (Sn), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 0.15 to 0.3 | |
| 0 |
| Zinc (Zn), % | 0 to 0.1 | |
| 13.9 to 22 |
| Residuals, % | 0 | |
| 0 to 0.5 |