A360.0 Aluminum vs. EN 1.3960 Stainless Steel

A360.0 aluminum belongs to the aluminum alloys classification, while EN 1.3960 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is A360.0 aluminum and the bottom bar is EN 1.3960 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 72
200
Elongation at Break, % 1.6 to 5.0
34
Fatigue Strength, MPa 82 to 150
220
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 27
78
Tensile Strength: Ultimate (UTS), MPa 180 to 320
590
Tensile Strength: Yield (Proof), MPa 170 to 260
270

Thermal Properties

Latent Heat of Fusion, J/g 530
290
Maximum Temperature: Mechanical, °C 170
970
Melting Completion (Liquidus), °C 680
1440
Melting Onset (Solidus), °C 590
1400
Specific Heat Capacity, J/kg-K 900
470
Thermal Conductivity, W/m-K 110
15
Thermal Expansion, µm/m-K 21
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 30
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 100
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
21
Density, g/cm3 2.6
7.9
Embodied Carbon, kg CO2/kg material 7.8
4.1
Embodied Energy, MJ/kg 150
57
Embodied Water, L/kg 1070
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.6 to 13
170
Resilience: Unit (Modulus of Resilience), kJ/m3 190 to 470
190
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 53
25
Strength to Weight: Axial, points 19 to 34
21
Strength to Weight: Bending, points 27 to 39
20
Thermal Diffusivity, mm2/s 48
3.9
Thermal Shock Resistance, points 8.5 to 15
17

Alloy Composition

Aluminum (Al), % 85.8 to 90.6
0
Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
16.5 to 18.5
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 0 to 1.3
60.2 to 67.9
Magnesium (Mg), % 0.4 to 0.6
0
Manganese (Mn), % 0 to 0.35
0 to 2.0
Molybdenum (Mo), % 0
2.5 to 3.0
Nickel (Ni), % 0 to 0.5
13 to 15
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 9.0 to 10
0 to 1.0
Sulfur (S), % 0
0 to 0.020
Tin (Sn), % 0 to 0.15
0
Zinc (Zn), % 0 to 0.5
0
Residuals, % 0 to 0.25
0