A360.0 Aluminum vs. EN 1.4805 Stainless Steel
A360.0 aluminum belongs to the aluminum alloys classification, while EN 1.4805 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is A360.0 aluminum and the bottom bar is EN 1.4805 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 75 | |
| 140 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 200 |
| Elongation at Break, % | 1.6 to 5.0 | |
| 9.0 |
| Fatigue Strength, MPa | 82 to 150 | |
| 130 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 27 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 320 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 170 to 260 | |
| 250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 530 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 1000 |
| Melting Completion (Liquidus), °C | 680 | |
| 1390 |
| Melting Onset (Solidus), °C | 590 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 480 |
| Thermal Conductivity, W/m-K | 110 | |
| 14 |
| Thermal Expansion, µm/m-K | 21 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 26 |
| Density, g/cm3 | 2.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 4.7 |
| Embodied Energy, MJ/kg | 150 | |
| 66 |
| Embodied Water, L/kg | 1070 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.6 to 13 | |
| 37 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 470 | |
| 150 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 53 | |
| 25 |
| Strength to Weight: Axial, points | 19 to 34 | |
| 17 |
| Strength to Weight: Bending, points | 27 to 39 | |
| 18 |
| Thermal Diffusivity, mm2/s | 48 | |
| 3.7 |
| Thermal Shock Resistance, points | 8.5 to 15 | |
| 11 |
Alloy Composition
| Aluminum (Al), % | 85.8 to 90.6 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.2 to 0.5 |
| Chromium (Cr), % | 0 | |
| 19 to 23 |
| Copper (Cu), % | 0 to 0.6 | |
| 0 |
| Iron (Fe), % | 0 to 1.3 | |
| 44.9 to 56.8 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 to 0.5 | |
| 23 to 27 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 9.0 to 10 | |
| 1.0 to 2.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.25 | |
| 0 |