A360.0 Aluminum vs. EN 1.5521 Steel
A360.0 aluminum belongs to the aluminum alloys classification, while EN 1.5521 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is A360.0 aluminum and the bottom bar is EN 1.5521 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 75 | |
| 130 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 190 |
| Elongation at Break, % | 1.6 to 5.0 | |
| 11 to 21 |
| Fatigue Strength, MPa | 82 to 150 | |
| 210 to 310 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 27 | |
| 73 |
| Shear Strength, MPa | 180 | |
| 310 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 180 to 320 | |
| 430 to 1390 |
| Tensile Strength: Yield (Proof), MPa | 170 to 260 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 530 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 400 |
| Melting Completion (Liquidus), °C | 680 | |
| 1460 |
| Melting Onset (Solidus), °C | 590 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 51 |
| Thermal Expansion, µm/m-K | 21 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 30 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 100 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 1.9 |
| Density, g/cm3 | 2.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 150 | |
| 19 |
| Embodied Water, L/kg | 1070 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.6 to 13 | |
| 44 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 470 | |
| 250 to 630 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 53 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 34 | |
| 15 to 49 |
| Strength to Weight: Bending, points | 27 to 39 | |
| 16 to 35 |
| Thermal Diffusivity, mm2/s | 48 | |
| 14 |
| Thermal Shock Resistance, points | 8.5 to 15 | |
| 13 to 41 |
Alloy Composition
| Aluminum (Al), % | 85.8 to 90.6 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 | |
| 0.16 to 0.2 |
| Copper (Cu), % | 0 to 0.6 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 1.3 | |
| 98 to 98.9 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 9.0 to 10 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 | |
| 0 to 0.025 |
| Tin (Sn), % | 0 to 0.15 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.25 | |
| 0 |