A384.0 Aluminum vs. AZ91E Magnesium
A384.0 aluminum belongs to the aluminum alloys classification, while AZ91E magnesium belongs to the magnesium alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is A384.0 aluminum and the bottom bar is AZ91E magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 74 | |
| 46 |
| Elongation at Break, % | 2.5 | |
| 2.5 to 6.2 |
| Fatigue Strength, MPa | 140 | |
| 81 to 85 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 28 | |
| 18 |
| Shear Strength, MPa | 200 | |
| 89 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 330 | |
| 160 to 260 |
| Tensile Strength: Yield (Proof), MPa | 170 | |
| 96 to 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 550 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 130 |
| Melting Completion (Liquidus), °C | 610 | |
| 600 |
| Melting Onset (Solidus), °C | 510 | |
| 500 |
| Specific Heat Capacity, J/kg-K | 880 | |
| 990 |
| Thermal Conductivity, W/m-K | 96 | |
| 84 |
| Thermal Expansion, µm/m-K | 21 | |
| 27 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 23 | |
| 10 to 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 73 | |
| 52 to 60 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 12 |
| Density, g/cm3 | 2.8 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 7.5 | |
| 22 |
| Embodied Energy, MJ/kg | 140 | |
| 160 |
| Embodied Water, L/kg | 1010 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 6.9 | |
| 3.4 to 12 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 100 to 190 |
| Stiffness to Weight: Axial, points | 15 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 69 |
| Strength to Weight: Axial, points | 32 | |
| 25 to 42 |
| Strength to Weight: Bending, points | 38 | |
| 37 to 53 |
| Thermal Diffusivity, mm2/s | 39 | |
| 49 |
| Thermal Shock Resistance, points | 15 | |
| 9.0 to 15 |
Alloy Composition
| Aluminum (Al), % | 79.3 to 86.5 | |
| 8.1 to 9.3 |
| Copper (Cu), % | 3.0 to 4.5 | |
| 0 to 0.015 |
| Iron (Fe), % | 0 to 1.3 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 to 0.1 | |
| 88.8 to 91.3 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.17 to 0.35 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 to 0.0010 |
| Silicon (Si), % | 10.5 to 12 | |
| 0 to 0.2 |
| Tin (Sn), % | 0 to 0.35 | |
| 0 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0.4 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |