A390.0 Aluminum vs. 390.0 Aluminum
Both A390.0 aluminum and 390.0 aluminum are aluminum alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is A390.0 aluminum and the bottom bar is 390.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 110 to 140 | |
120 |
Elastic (Young's, Tensile) Modulus, GPa | 75 | |
75 |
Elongation at Break, % | 0.87 to 0.91 | |
1.0 |
Fatigue Strength, MPa | 70 to 100 | |
76 to 110 |
Poisson's Ratio | 0.33 | |
0.33 |
Shear Modulus, GPa | 28 | |
28 |
Tensile Strength: Ultimate (UTS), MPa | 190 to 290 | |
280 to 300 |
Tensile Strength: Yield (Proof), MPa | 190 to 290 | |
240 to 270 |
Thermal Properties
Latent Heat of Fusion, J/g | 640 | |
640 |
Maximum Temperature: Mechanical, °C | 170 | |
170 |
Melting Completion (Liquidus), °C | 580 | |
650 |
Melting Onset (Solidus), °C | 480 | |
560 |
Specific Heat Capacity, J/kg-K | 880 | |
880 |
Thermal Conductivity, W/m-K | 130 | |
130 |
Thermal Expansion, µm/m-K | 20 | |
18 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 20 | |
24 to 25 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 67 | |
79 to 83 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 11 | |
11 |
Density, g/cm3 | 2.7 | |
2.7 |
Embodied Carbon, kg CO2/kg material | 7.3 | |
7.3 |
Embodied Energy, MJ/kg | 140 | |
130 |
Embodied Water, L/kg | 950 | |
950 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.6 to 2.6 | |
2.7 to 2.9 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 580 | |
380 to 470 |
Stiffness to Weight: Axial, points | 15 | |
15 |
Stiffness to Weight: Bending, points | 52 | |
52 |
Strength to Weight: Axial, points | 19 to 30 | |
28 to 30 |
Strength to Weight: Bending, points | 27 to 36 | |
35 to 36 |
Thermal Diffusivity, mm2/s | 56 | |
56 |
Thermal Shock Resistance, points | 9.0 to 14 | |
14 to 15 |
Alloy Composition
Aluminum (Al), % | 75.3 to 79.6 | |
74.5 to 79.6 |
Copper (Cu), % | 4.0 to 5.0 | |
4.0 to 5.0 |
Iron (Fe), % | 0 to 0.5 | |
0 to 1.3 |
Magnesium (Mg), % | 0.45 to 0.65 | |
0.45 to 0.65 |
Manganese (Mn), % | 0 to 0.1 | |
0 to 0.1 |
Silicon (Si), % | 16 to 18 | |
16 to 18 |
Titanium (Ti), % | 0 to 0.2 | |
0 to 0.2 |
Zinc (Zn), % | 0 to 0.1 | |
0 to 0.1 |
Residuals, % | 0 | |
0 to 0.2 |